ON THE MECHANISM OF ORIGIN AND DESTRUCTION OF ELEMENTS OF CARBON STEEL FOR STATIC TENSION

Authors

Moyseychik E.A., Candidate of Technical Sciences, Associate Professor of the Department "Strength of Materials and Elasticity Theory", Belarusian National Technical University, Minsk, Republic of Belarus, This email address is being protected from spambots. You need JavaScript enabled to view it.

In the section TECHNOLOGICAL MECHANICS
Year 2011 Issue 4 Pages 80-86
Type of article RAR Index UDK 620.17 Index BBK  
Abstract In the article on the basis of experimental data to investigate the mechanism of nucleation and crack development in the vicinity of defects in static tensile sheet elements of mild steel. It is shown that the destruction is initiated by the initial crack of a parabolic shape, emerging from defects in design-technological origin. Based on the correlations found that the shape and size of the initial cracks are determined by the volume of plastically deformed material at the base of the defect and the physical and chemical processes taking place in this volume. By using infrared heat deformation shows that the material of a deformable element for loading the formation of blocks with different stress-strain state. It is suggested that the development of initial cracks in elastically strained unit determines its brittle fracture and crack propagation along the trajectories of maximum shear stress leads to ductile fracture specimen.
Keywords

static stretching, crack, loading, stress-strain state, low-carbon steel

  You can access full text version of the article.
Bibliography
  • Makklintok F., Argon A. Deformacija i razrushenie materialov [Deformation and fracture of materials]. Moscow, Mir,1970. 444 p.
  • Fridman Ja.B. Mehanicheskie svojstva metallov [Mechanical properties of metals]. Chast 2, Mehanicheskie ispytanija. Konstrukcionnaja prochnost' [Part 2: Mechanical tests. Structural strength]. Moscow, Mashinostroenie, 1974. 368 p.
  • Augustin Ja., Shledzevskij E. Avarii stal'nyh konstrukcij [Accidents of steel structures]. Moscow, Strojizdat, 1978. 183 p.
  • Nott Dzh. Osnovy mehaniki razrushenii [Fundamentals of fracture mechanics]. Moscow, Metallurgija, 1978. 256 p.
  • Broek D. Osnovy mehaniki razrushenija [Fundamentals of fracture mechanics]. Moscow, Vyssh.shk., 1980. 368 p.
  • Mojsejchik E.A. Kolichestvennaja ocenka nadezhnosti staticheski rastjanutyh jelementov stroitel'nyh konstrukcij iz malouglerodistyh stalej pri nizkih temperaturah. Diss. kand. tehn. nauk: [Quantitative assessment of reliability statically of stretched construction elements from low-carbon steels at low temperatures. Cand. techn. sci. diss.]. Novosibirsk, 1980. 205 p.
  • Straus B., Fry Ad. Riβbildung in Kesselblechen. Stahl und Eisen, 1921, no. 33, pp. 1133-1137.
  • Fry Ad. Kraftwirkungfiguren im Flubeisen, dargestelt durch ein neues Aetzverfahren. Stahl und Eisen, 1921, no. 32, pp. 1093-1097.
  • Rudeloff M. Berichte des Ausschusses fur Versuche im Eisenbau. Ausgabe A. Heft 3: Versuche mit Auschlussen steifer Stube. Berlin: Verlag von J.Springer, 1921. 84p.
  • Nadai A. Der Bildsame Zustand der Werkstoffe. Berlin, Verlag von J. Springer, 1927. 171p.
  • Hort W. Handbuch der Physikalischen und technischen Mechanik. Band IV-2 Halfte. Technische Physik der festen Korper. Herausgegeben von prof. F. Auerbach. Berlin, Verlag fur J. Springer, 1931. 614p.